Fiberglass Rod FRP Rods for Composite Insulator:
1. Capacity of fiber glass rod/fiberglass rod: 100 Pultrusion lines, the largest manufacturer of composite insulator rods in China.
2. Technique of fiber glass rod/fiberglass rod : The only one using vacuum injection technique without mould release agent, Patent No. 200610041850.1.
3. Test of fiber glass rod/fiberglass rod : Rods passed tests in domestic labs, including WHVRI, CEMT, XIHARI, especially passed KEMA tests in the Netherlands and 7200h stress corrosion test.
4. Standards: IEC61109 IEC61952, ANSI C29.13-2000, GB/T19519, DL/T810 DL/T864
5. Application: The rods of Taporel have been applied in the highest voltage(1000kv) AC transmission lines & applied in the highest voltage(± 800kv) DC transmission lines.
2. Specifications:
Diameter 5mm-130 mm; Length according to customer's order
3. Classify:
3.1Based on properties, rods are classified into High temperature resistant type (E-glass Rod) and High temperature & acid resistant type (ECR-glass Rod).
3.2Based on properties, rods are classified into High temperature resistant type (E-glass Rod) and High temperature & acid resistant type (E-glass Rod)
3.3Based on application, fiberglass rods are classified into 7 types:
For composite suspension & tension insulators (Diameter 16mm- 40mm)
For composite pin insulators((Diameter 24mm---53mm)
For composite cross arm insulators(Diameter 28mm- 80mm)
For composite post insulator (Diameter 28mm- 130mm)
For composite surge arresters(Diameter 5mm- 40mm)
For composite fuse cutout (Diameter 19mm- 36mm)
3.3. Color: Light green, brown, black
2. Our products:
3. Our worshop:
1. Capacity of fiber glass rod/fiberglass rod: 100 Pultrusion lines, the largest manufacturer of composite insulator rods in China.
2. Technique of fiber glass rod/fiberglass rod : The only one using vacuum injection technique without mould release agent, Patent No. 200610041850.1.
3. Test of fiber glass rod/fiberglass rod : Rods passed tests in domestic labs, including WHVRI, CEMT, XIHARI, especially passed KEMA tests in the Netherlands and 7200h stress corrosion test.
4. Standards: IEC61109 IEC61952, ANSI C29.13-2000, GB/T19519, DL/T810 DL/T864
5. Application: The rods of Taporel have been applied in the highest voltage(1000kv) AC transmission lines & applied in the highest voltage(± 800kv) DC transmission lines.
2. Specifications:
Diameter 5mm-130 mm; Length according to customer's order
3. Classify:
3.1Based on properties, rods are classified into High temperature resistant type (E-glass Rod) and High temperature & acid resistant type (ECR-glass Rod).
3.2Based on properties, rods are classified into High temperature resistant type (E-glass Rod) and High temperature & acid resistant type (E-glass Rod)
3.3Based on application, fiberglass rods are classified into 7 types:
For composite suspension & tension insulators (Diameter 16mm- 40mm)
For composite pin insulators((Diameter 24mm---53mm)
For composite cross arm insulators(Diameter 28mm- 80mm)
For composite post insulator (Diameter 28mm- 130mm)
For composite surge arresters(Diameter 5mm- 40mm)
For composite fuse cutout (Diameter 19mm- 36mm)
3.3. Color: Light green, brown, black
no | parameter | unit | specification |
| 1 | Density(at 20±2) | g/cm 3 | 2.2 |
| 2 | Water absorbtion rate (at20±2,24h) | % | 0.05 |
| 3 | Tensile strength | Mpa | 1690 |
| 4 | Bending strength | Mpa | 1100 |
| 5 | Dry penetration test | Min | 50 |
| 6 | Water difussion test(1%nacl,boiling for 100h 12kv/1min) | μA | <10 |
| 7 | Shearing strength along laminals | Mpa | 50 |
| 8 | Volume resistivity(140,96h) | Ω.M | 10 10 |
| 9 | DC withstand voltage(10min) | kV | 50 |
| 10 | Lightning surge withstand voltage(100kv,10mm) | times | 5 |
| 11 | Bending strength at heating conditions | Mpa/150 | 350 |
| 12 | Stress corrosion (1 mol/1hno3,at 67% stress) | h | 7200 |
| 13 | Torsion strength | Mpa | 800 |
2. Our products:
3. Our worshop: